There was a need to define the spatial density of stress-corrosion crack arrays that develop in operating gas-transmission pipelines and in laboratory test specimens of line-pipe steel, to improve understanding of the factors that control the density and provide data to test models of pipeline cracking. Within the broad definition of crack density are included the locations, numbers, lengths, depths, and degree of linkage of cracks. An analysis has been conducted of location, numbers, lengths, depths, and degree of linkage of stress-corrosion crack colonies in samples from the field and from ...
There was a need to define the spatial density of stress-corrosion crack arrays that develop in operating gas-transmission pipelines and in laboratory test specimens of line-pipe steel, to improve understanding of the factors that control the density and provide data to test models of pipeline cracking. Within the broad definition of crack density are included the locations, numbers, lengths, depths, and degree of linkage of cracks. An analysis has been conducted of location, numbers, lengths, depths, and degree of linkage of stress-corrosion crack colonies in samples from the field and from laboratory tests. This has provided data to test any model of the cracking of pipelines. Thus, it is shown that crack densities are of the order of 5 cracks/mm of distance normal to the crack length direction and that the depths and lengths of cracks are distributed according to log normal and Weibull functions. During the growth stage of cracks in a colony, their spatial distribution is not random, because of the interaction of their associated stress fields. That interaction also results in the coalescence of cracks, an extremely important part of the overall growth process, and that interaction is defined quantitatively to provide further information to which modeling must aspire.